Kuat Tekan Mortar Berbasis Serat Kelapa dan Limbah Kaca
Abstract
This study aims to determine the effect of using glass waste and coconut fiber in mortar with various percentages, namely 0%, 5%, 10%, 15% glass powder and 0%, 1%, 2% coconut fiber with a total of 21 test objects, then testing was carried out after the test objects were 28 days old. The test results showed that the addition of coconut fiber and glass powder with a percentage of coconut fiber of 1% and glass powder of 5%, 10%, 15% in the mortar mixture increased the compressive strength by 17.65 MPa, 18.57 MPa, and 25.36 MPa. However, the addition of coconut fiber by 2% and glass powder 5%, 10%, 15% decreased the compressive strength to 16.97 Mpa, 16.68 Mpa, and 16.44 Mpa.
Keywords
Full Text:
PDFReferences
Anonim. 2022,Panduan Penulisan Tugas Akhir Program Studi Teknik Sipil Universitas Abulyatama, Universitas Abulyatama LampohKeudee Aceh Besar.
ANUAR, M, 2020,Pengaruh Penambahan Serat Kulit Kayu Andilau (Commersonia Bartramia).
ASTM International, 2021, ASTM C109 / C109M-20a, Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in, or [50-mm] Cube Specimens), ASTM International.
ASTM International, 2021, ASTM C307-03, Standard Test Method for Tensile Strength of Chemical-Resistant Mortar, Grouts, and Monolithic Surfacings, ASTM International.
Anggi, H. R. L., Rahmawati, C., & Sriana, T. (2023). Kekuatan Tekan Dan Lentur Mortar Berbasis Serat Kelapa Dan Serbuk Limbah Kaca. Prosiding SEMDI-UNAYA (Seminar Nasional Multi Disiplin Ilmu UNAYA).
Çomak, B., Bideci, A., & Salli Bideci, Ö, 2018,Effects of hemp fibers on characteristics of cement based mortar, Construction and Building Materials, 169, 794–799. https://doi.org/10.1016/J.CONBUILDMAT.2018.03.029
Cut Rahmawati, 2021,Preparation and Characterization of Cellulose Nanocrystals from Typha sp. as a Reinforcing Agent, Universitas Abulyatama, Aceh Besar.
Istiqomah, 2013,Workability Dan Kuat Tekan Mortar Dengan Sabut Kelapa, Program studiTeknik Sipil Universitas Pendidikan Indonesia, Bandung.
Londok, M. P. M., Supit, S. W. M., & Rangkang, J, 2022,Pengaruh Pemanfaatan Serat Selulosa Bambu Terhadap Kuat Tekan Dan Penyusutan Campuran Mortar, Seminar Nasional Terapan Riset Inovatif (SENTRINOV) Ke-8.
Meliyana, M., Rahmawati, C., & Handayani, L. (2019). Sintesis Nano Silika dari Abu Sekam Padi Dengan Metode Sol-Gel. Seminar Nasional Multi Disiplin Ilmu Universitas Asahan Ke-3, 800–807.
Nasir, M., Aziz, M. A., Zubair, M., Ashraf, N., Hussein, T. N., Allubli, M. K., Manzar, M. S., Al-Kutti, W., & A. Al-Harthi, M, 2022, Engineered cellulose nanocrystals-based cement mortar from office paper waste: Flow, strength, microstructure, and thermal properties, Journal of Building Engineering, 51, 104345. https://doi.org/10.1016/J.JOBE.2022.104345
Rahmawati, C., Faisal, M., Ahmad, J., & Muliana, I. (2025). Extraction and characterization of nanocellulose from bemban fibre for cement-based composite. Case Studies in Construction Materials, 22.
Rahmawati, C., Zardi, M., Anggi, H. R. L., & Akhramurizqi. (2024). Current development of waste glass as building construction materials. AIP Conference Proceedings.
DOI: https://doi.org/10.30601/jtsu.v11i1.5582
Refbacks
- There are currently no refbacks.
Copyright (c) 2025 Firanalia Firanalia, Cut Rahmawati, Mery Silviana
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Jurnal Teknik Sipil Unaya
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
© Jurnal Teknik Sipil Unaya : Published by Center for Research and Community Service (LPPM) University of Abulyatama, Aceh, Indonesia. 2019