Pengaruh Penambahan POFA dan Sika Latex pada Kekuatan Mekanis Papan Semen sebagai Dinding Bangunan

Santi Wiranda; Muhammad Zardi; Cut Rahmawati

doi:10.30601/jtsu.v12i2.7753

Pengaruh Penambahan POFA dan Sika Latex pada Kekuatan Mekanis Papan Semen sebagai Dinding Bangunan

Santi Wiranda, Muhammad Zardi, Cut Rahmawati

Abstract

The use of environmentally friendly materials in construction continues to grow along with the increasing need to reduce carbon emissions from the cement industry. One alternative material that can be utilized is Palm Oil Fuel Ash (POFA), which is a waste product from the combustion of palm oil residues. This study aims to analyze the effect of adding POFA and Sika Latex on the mechanical strength of mortar as a base material for cement boards. The POFA variations used were 0%, 5%, 10%, and 15% as partial substitutes for cement, while the ratio variations of water to Sika Latex were 0, 1:0.5, 1:1, and 1:1.5. Testing was conducted on compressive strength using cube specimens measuring 5×5×5 cm and flexural strength using beam specimens measuring 4×4×16 cm at 28 days of curing age. The results showed that the use of 5% POFA with a water to Sika Latex ratio of 1:1 produced the optimum compressive strength of 17.44 MPa. Meanwhile, the highest flexural strength value of 0.86 MPa was obtained in the mixture without POFA with a Sika Latex ratio of 1:1.5. The results indicate that POFA is more effective in improving the compressive strength of mortar, while Sika Latex plays a more dominant role in enhancing flexural strength.

Keywords

POFA, Sika Latex, Mortar, Papan Semen, Kuat Tekan, Kuat Lentur.

Full Text:

PDF

References

Hidayat, R., Wahyudi, A., & Kusuma, T. (2024). Analisis Potensi Limbah Agroindustri Kelapa Sawit sebagai Material Konstruksi Berkelanjutan di Indonesia. Jurnal Teknik Sipil dan Lingkungan, 9(1), 45-58.

Ahmad, A. B., & Hassan, S. M. (2018). Mechanical Properties of Mortar with Palm Oil Fuel Ash (POFA) as a Partial Cement Replacement. Journal of Civil Engineering, 15(2), 123-130.

Ahn, J., Lee, S., & Park, H. (2023). "Durability of polymer-modified concrete in chloride environment." Journal of Marine Structures, 8(2), 112-125.

Al-Jabri, A. S., Hago, A. W., & Al-Nuaimi, A. S. (2020). "Performance of concrete with palm oil fuel ash as a partial cement replacement." Construction and Building Materials, 239, 117865.

Prasetyo, B., Utomo, S., & Widodo, M. (2021). Evaluasi Jejak Karbon Industri Semen Portland dan Strategi Mitigasi Melalui Material Pozzolan Alternatif. Jurnal Teknologi Bahan Bangunan, 12(3), 112-125.

Aulia, Z., Rahmawati, E., & Handayani, M. (2020). Pengaruh Penggunaan Abu Cangkang Sawit (POFA) sebagai Bahan Pengganti Semen terhadap Kuat Tekan dan Kuat Lentur Mortar. Jurnal Rekayasa Sipil, 6(1), 45-56.

Rahmawati, D. (2023). Pengaruh Penambahan Emulsi Polimer Latex terhadap Sifat Mekanis dan Mikrostruktur Mortar Semen. Rekayasa Hijau: Jurnal Teknologi Ramah Lingkungan, 7(2), 89-102.

Hassan, M. S., & Aziz, A. M. (2021). Palm Oil Fuel Ash-Based Eco-Friendly Concrete Composite: A Critical Review of the Long-Term Properties. Materials, 14(22), 7074.

Sika Indonesia. (2022). Lembar Data Teknis Sika® Latex: Bahan Tambah Emulsi Polimer untuk Mortar dan Perekat. Bogor: PT Sika Indonesia.

Wijaya, K., & Saputra, H. (2022). Karakterisasi Palm Oil Fuel Ash (POFA) sebagai Material Substitusi Semen dalam Pembuatan Beton Mutu Tinggi. Jurnal Riset Konstruksi Indonesia, 15(4), 210-222.

Mehta, P. K., & Monteiro, P. J. M. (2014). Concrete: Microstructure, Properties, and Materials. McGraw-Hill Education. (Sumber ini memberikan wawasan mendalam tentang komposisi, mikrostruktur, dan karakteristik bahan-bahan konstruksi, termasuk semen dan mortar).

SNI 03-2105-2006. Papan Semen Partikel. Badan Standardisasi Nasional. Jakarta.

Neville, A. M. (2011). Properties of Concrete. Prentice Hall. (Buku ini merupakan referensi klasik yang membahas secara mendalam tentang sifat- sifat beton dan material penyusunnya, termasuk mortar).

Putri, S. A., & Kurniawan, D. (2023). Eksperimen Kuat Lentur Papan Semen Serat dengan Bahan Tambah Latex Polimer. Jurnal Teknik Bahan Bangunan, 14(1), 40-52.

Pai, B.H.V., Nandy, M., Krishnamoorthy, A., & Sarkar, P.K. (2014). Particle Packing Approach for Designing the Mortar Phase of Self Compacting Concrete. Makalah dipresentasikan pada International Conference on Sustainable Civil Infrastructure (ICSCI 2014).

Zulkarnain, F. (2021). Efektivitas Penggunaan SBR-Latex terhadap Sifat Kedap Air dan Elastisitas Panel Dinding Prefabrikasi. Jurnal Riset Teknologi Sipil, 5(2), 95-108.

Arifi, E. (2022). Analisis Mikrostruktur Mortar Modifikasi Polimer SBR terhadap Ketahanan Sulfat. Jurnal Rekayasa Sipil, Vol. 16, No. 2.

Rahmawati, D. (2023). Karakteristik Mekanis Mortar dengan Campuran Polimer Sintetis. Jurnal Inovasi Material Bangunan, Vol. 5, No. 1.

Taufik, R. (2021). Studi Penggunaan Abu Terbang (Fly Ash) dan Abu Cangkang Sawit (POFA) sebagai Bahan Pengisi Beton Ringan. Tesis, Universitas Gadjah Mada.

Santoso, B. (2024). Pengaruh Polimer terhadap Workabilitas dan Kuat Tekan Mortar Mutu Tinggi. Jurnal Konstruksi dan Infrastruktur, Vol. 12, No. 3.

Unaidi, M. Z., & Zulkifli, M. Z. (2021). Palm Oil Fuel Ash-Based Eco-Friendly Concrete Composite: A Critical Review of the Long-Term Properties. Materials, 14(22), 7074.

Prasetyo, B. (2021). Evaluasi Jejak Karbon Industri Semen Portland dan Strategi Mitigasi. Jurnal Teknologi Bahan Bangunan.

Rahmawati, D. (2023). Pengaruh Penambahan Emulsi Polimer Latex terhadap Sifat Mekanis dan Mikrostruktur Mortar Semen. Rekayasa Hijau.

Santoso, A. (2024). Optimalisasi Kuat Lentur Papan Semen Berbasis Abu Terbang dan Polimer Sintetis. Media Komunikasi Teknik Sipil.

Wijaya, K., & Saputra, H. (2022). Karakterisasi Palm Oil Fuel Ash (POFA) sebagai Material Substitusi Semen. Jurnal Riset Konstruksi Indonesia.

Zulkarnain, F. (2021). Efektivitas SBR-Latex terhadap Sifat Kedap Air dan Elastisitas Panel Dinding. Jurnal Riset Teknologi Sipil

Hasanah, N. (2024). Pengaruh Kehalusan Partikel POFA terhadap Stabilitas Dimensi dan Kuat Tekan Mortar Hijau. Jurnal Infrastruktur dan Rekayasa Sipil, 12(1), 22-35.

Lestari, W., & Utomo, P. (2023). Mekanisme Reaksi Pozzolanik pada Beton Geopolimer dan Mortar Substitusi POFA. Jurnal Material dan Struktur, 7(3), 145-158.

Lubis, A. M., Nasution, A., & Sinaga, F. (2021). Pemanfaatan Abu Terbang Kelapa Sawit sebagai Bahan Pengganti Semen pada Beton Normal. Jurnal Teknik Sipil dan Arsitektur, 26(2), 77-85.

Ramadhani, S., & Fitri, A. (2023). Sustainability in Construction: A Review of Palm Oil Fuel Ash (POFA) as a Cementitious Material in Indonesia. International Journal of Sustainable Building Technology, 15(4), 112-126.

Sika Indonesia. (2022). Lembar Data Teknis Sika® Latex: Bahan Tambah Emulsi Polimer untuk Mortar. Bogor: PT Sika Indonesia.

DOI: https://doi.org/10.30601/jtsu.v12i2.7753

Refbacks

There are currently no refbacks.

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

Jurnal Teknik Sipil Unaya

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.