Pengaruh Variasi Konsentrasi Larutan Naoh 6m Dan 8m Terhadap Penurunan Caco3 Pada Mortar Geopolimer Berbahan Dasar Fly Ash Nagan Raya

Penulis

DOI:

https://doi.org/10.30601/jtsu.v7i1.1505

Kata Kunci:

geopolimer, kalsium karbonat, fly ash Nagan Raya

Abstrak

The combination of NaOH and Na2SiO3 in an alkaline solution is able to react with FA  to form Si-O-Si and Si-O-Al gels. Several studies have shown that the high concentration of NaOH causes the appearance of calcium carbonate (CaCO3) on the surface of the specimen. This problem became the concern of this study, the reduction NaOH concentration was investigated to reduce CaCO3. The results showed that the chemical composition of FA Nagan Raya (FANR) contained Si, Al, and Ca compounds which were respectively around 37.16%, 17.61%, and 8.72%. XRD analysis shows that the main peaks of the FANR material and paste are in the 20 to 30 2θ region. FTIR analysis showed that the peak of the band 1380cm-1 - 1450cm-1, showed that the CaCO3 was bent in the FANR paste. The TGA analysis shows that the weight loss of FANR paste is higher than material of FANR. Low NaOH concentration has decreasing workability which causes faster setting time and reduces compressive strength. However, the use of a low concentration of NaOH solution can reduce CaCO3 on the surface of spesimen.

Biografi Penulis

  • Aiyub Aiyub, Politeknik Negeri Lhokseumawe
    Jurusan Teknik Sipil
  • Fajri Fajri, Politeknik Negeri Lhokseumawe
    Jurusan Teknik Sipil

Referensi

Chindaprasirt, P., De Silva, P., Sagoe-Crentsil, K., & Hanjitsuwan, S. (2012). Effect of SiO 2 and Al 2O 3on the setting and hardening of high calcium fly ash-based geopolymer systems. Journal of Materials Science. https://doi.org/10.1007/s10853-012-6353-y

Davidovits, J. (1998). Geopolymer chemistry and properties. 1st European Conference on Soft Mineralurgy, Compiegne, France, 1, 25–48.

Davidovits, J. (2013). Geopolymer Cement a review. Geopolymer Science and Technics.

Owaid, H. M., Hamid, R. B., & Taha, M. R. (2012). A review of sustainable supplementary cementitious materials as an alternative to all-portland cement mortar and concrete. In Australian Journal of Basic and Applied Sciences (Vol. 6, Issue 9, pp. 287–303).

Rahmawati, C., Aprilia, S., Saidi, T., & Aulia, T. B. (2021). Mineralogical, Microstructural and Compressive Strength Characterization of Fly Ash as Materials in Geopolymer Cement. Elkawnie, 7(1), 1–17.

Rahmawati, C., & Meliyana, M. (2019). Potensi Limbah Karbit Sebagai Pengganti Semen Pada Bata Ringan. Seminar Nasional Multi Disiplin Ilmu Universitas Asahan, 627–635.

Rahmawati, C., Meliyana, M., Thufail, I., Muhtadin, M., & Faisal, M. (2020). Impact of Fire on Mechanical Properties of Lightweight Bricks Containing Calcium Carbide Residue. Jurnal Inotera, 5(2), 129–138.

Singh, N. B. (2018). Fly ash-based geopolymer binder: A future construction material. In Minerals (Vol. 8, Issue 7). MDPI AG. https://doi.org/10.3390/min8070299

Unduhan

Diterbitkan

2021-01-19

Terbitan

Vol 7 No 1 (2021): Januari 2021

Bagian

Artikel

Lisensi

Proposed Policy for Journals That Offer Open Access Authors who publish with Jurnal Teknik Sipil Unaya agree to the following terms: a. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal. b. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal. c. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).

Cara Mengutip

Pengaruh Variasi Konsentrasi Larutan Naoh 6m Dan 8m Terhadap Penurunan Caco3 Pada Mortar Geopolimer Berbahan Dasar Fly Ash Nagan Raya. (2021). Jurnal Teknik Sipil Unaya, 7(1), 12-22. https://doi.org/10.30601/jtsu.v7i1.1505